Effects of trace amount modified SiC nanoparticles and processing parameters on microstructure and mechanical properties of ZA27 alloy

ABSTRACT

In order to strengthen and obtain the optimised processing parameters during the modified SiC nanoparticles reinforce ZA27 alloys. The present investigation deals with the effects of trace amount modified SiC nanoparticles and processing parameters on the microstructures and mechanical properties of ZA27 alloy. The results indicate that the microstructures are effectively refined by the modified SiC nanoparticles. It’s likely to fade the refined effect for the modified SiC nanoparticles to raise the addition temperature, prolong the holding time, increase the pouring temperature and enhance the cooling rate. In this experiment, when the addition amount is 0.5%, the addition temperature is 680°C, the holding time is 3 min, the pouring temperature is 600°C and the mould is preheated at 200°C, the microstructure and mechanical properties of ZA27 alloy are better. The action mechanisms of the modified SiC nanoparticles and processing parameters are also discussed.

KEYWORDS:

• ZA27 alloy
• microstructure
• modified SiC nanoparticles
• processing parameters
• mechanical properties

Disclosure statement

No potential conflict of interest was reported by the author(s).

Data availability statement

Data sharing is not applicable to this article as no new data were created or analysed in this study.

Additional information

Funding

This work was supported by the [National Natural Science Foundation of China] under Grant [Nos. 52171134, 51901033, 51204028]; [Dalian Science and Technology Innovation Foundation of Applied Basic Research] under Grant [No. 2022JJ12GX039]; [Dalian Outstanding Young Scientific and Technological Talents Project] under Grant [No. 2022RY14]; [Natural Science Foundation of Liaoning Province] under Grant [No. 2020-BS-207] and [Dalian High-level Talents Innovation Support Program] under Grant [No. 2016RQ052].