Diagnosis of durability-related problems in concrete structures through comprehensive analysis and non-destructive testing: a case study

ABSTRACT

The present study investigated concrete durability problems at the National University of Sciences and Technology,Pakistan, through comprehensive analysis and non-destructive testing. During the visual inspection of concrete structures, different deterioration mechanisms such as alkali-silica aggregate reaction (ASR), carbonation, abrasion and drying shrinkage were found. After visual inspection, the data on ingredients used in the construction of various structures were collected, revealingthat different brands of cement used in construction contained high alkali-equivalent content. Fine aggregates were used from two different quarries during construction. The available literature and X-ray Diffraction (XRD) results showed that both the quarries’ aggregates have the potential for alkali-silica reactivity. Furthermore, the XRD results of gel-type material collected from mapped cracking indicated the presence of delhayelite, similar to alkali-silica gel, suggesting ASR. The XRD curves of the whitest powder collected from various sites showed the presence of sodium sulfate and calcium carbonate peaks, indicating salt hydration attacks. The carbonation rate in concrete ranges from 4.33 to 5.77 mm/year. The results of the rebound hammer and pulse velocity test indicated that concrete used in parking has low strength which is the main cause of abrasion. Based on these findings a few recommendations have been presented to avoid durability-related problems in future structures.

KEYWORDS:

• Durability
• physical salt weathering
• alkali-aggregate reaction
• alkali-silica reaction
• carbonation rate
• case study

Acknowledgments

The authors are thankful to Asfar Abbas and Hamza Khalid of NUST Institute of Civil Engineering (NICE), the National University of Sciences and Technology (NUST), Pakistan for their valuable suggestions and help during the experimental phase.

Disclosure statement

No potential conflict of interest was reported by the author(s).